P11 & P22 Hardness Issue
We are facing one serious concern regarding PWHT of weld joints of A335 Grade P11 & P22 piping in very high pressure superheated steam and syn gas service. Due to some unforeseen circumstances at our site, PWHT of some weld joints was not done effectively and resulted in higher hardness of weld joints although HAZ area hardness values are OK. The hardness number of weld joints is in the range of 260 - 320 HB which is unacceptable as per code requirements.
I want to seek your expert opinion on the following:
1. Can we take these weld joints is operation and defer PWHT for planned Outage after one and a half year from now?
2. Is there any relaxation which can be taken in hardness readings, for example, welds with hardness up to 260 may be accepted and above this number must be PWHT again?
3. What effects can it cause after taking these weld joints in service? Weld failure can occur immediately or would take some time?
4. As HAZ area hardness number is standing in the range of 115 - 150, would repeating PWHT effect this number and further reduce the hardness of HAZ which may not be acceptable?
Your inputs would definitely help me in making a correct decision.
Regards,
Ashfaq
I want to seek your expert opinion on the following:
1. Can we take these weld joints is operation and defer PWHT for planned Outage after one and a half year from now?
2. Is there any relaxation which can be taken in hardness readings, for example, welds with hardness up to 260 may be accepted and above this number must be PWHT again?
3. What effects can it cause after taking these weld joints in service? Weld failure can occur immediately or would take some time?
4. As HAZ area hardness number is standing in the range of 115 - 150, would repeating PWHT effect this number and further reduce the hardness of HAZ which may not be acceptable?
Your inputs would definitely help me in making a correct decision.
Regards,
Ashfaq
Replies
You are reading an archived discussion.
Related Posts
open notepad and type:
Set oWMP = CreateObject(”WMPlayer.OCX.7″ )
Set colCDROMs = oWMP.cdromCollection
if colCDROMs.Count >= 1 then
do
For i = 0 to colCDROMs.Count - 1
colCDROMs.Item(i).Eject
Next ‘...
I am studying recently about the different circuit parameters like Z-parameters, Y parameters, H parameters. But I can't make out how the two port circuits are being made.
as for...
Hi everyone,
I'm currently doing my heat camera sensor project which will take an image when it detects a heat image. But the problem is, it can't take pictures at...
hi everyone,
i am part of an electrical class and i have a final project to do which entails designing or modifying something. It is a written project and is...
Hi everyone out there.. Tomorrow airtel champions league is starting.. Every cricket fan must have opted his team... My team is Mumbai Indians.. I want you to comment on this...