Hello, I need your help about Refractory

eng. · 2009-08-09T00:18:17+00:00

Dears, Do you have any Idea about Refractory? I would like to know about refractory more details. I know it is used for resistance high tempurature. In addition, If you have any books or any information that can help me, Please do not hesitate tell me. Thanks a lot all. 😁

Hello, I need your help about Refractory

eng.

Member

Updated: Oct 26, 2024

Views: 917

Dears,

Do you have any Idea about Refractory?
I would like to know about refractory more details. I know it is used for resistance high tempurature.

In addition, If you have any books or any information that can help me, Please do not hesitate tell me.

Thanks a lot all.

😁

0

Replies

Howdy guest!

Dear guest, you must be logged-in to participate on CrazyEngineers. We would love to have you as a member of our community. Consider creating an account or login.

Replies

eng.

Member • Aug 10, 2009

oh nobody replay? are you there. Can you Help me My friends?

Thank you very much.

Are you sure? This action cannot be undone.
Cancel
tashirosgt

Member • Aug 10, 2009

Do you need a handbook?
#-Link-Snipped-#

Are you sure? This action cannot be undone.
Cancel
itchap

Member • Aug 10, 2009

I Think this will helpful for you.......

<a href="https://en.wikipedia.org/wiki/Refractory" target="_blank" rel="nofollow noopener noreferrer">Refractory</a>

Are you sure? This action cannot be undone.
Cancel
eng.

Member • Aug 10, 2009

Thank you it chap. I have read this artical. But, I would like to know more information on refractory. and if you know a book for basic information and easy language by english, do not hesitate to tell me.

Thanks .

Are you sure? This action cannot be undone.
Cancel
rajeevsshastri

Member • Aug 11, 2009

eng.
oh nobody replay? are you there. Can you Help me My friends?

Thank you very much.
Dear friend
pl refer following is codes

IS: 1528 (Part I)-1974

DETERMINATION OF PYROMETRIC CONE EQUIVALENT (PCE) OR SOFTENING POINT

IS: 1528 (Part II) – 1974
Determination of refractoriness under load

IS : 1528 (Part III)- 1974
Determination of spalling resistance

IS: 1528 (Part IV)- 1974
Determination of cold crushing strength

IS: 1528 (Part V) – 1974
Determination of modulus of rupture

IS: 1528 (Part VI) – 1974
Determination of permanent change after reheating

IS: 1528 (Part VII) – 1974
Methods of sampling and criteria for conformity

IS: 1528 (Part VIII) – 1970
Determination of apparent porosity

IS: 1528 (Part IX) – 1980
Determination of true specific gravity and true density

IS: 1528 (Part X) – 1974
Determination of size of refractory bricks

IS: 1528 (Part XI) – 1974
Determination of warpage

IS: 1528 (Part XII) – 1974
Determination of bulk density

IS: 1528 (Part XIII) – 1974
Determination of resistance to the disintegration effect of carbon monoxide

IS: 1528 (Part XIV) – 1974
Sieve analysis

for details send your e- mail id to <removed. All discussions should happen through the forums for the benefit of everyone.>
regards
rajeevsshastri

Are you sure? This action cannot be undone.
Cancel
eng.

Member • Aug 11, 2009

thank you very much rajeevsshastri.

Are you sure? This action cannot be undone.
Cancel
alpac

Member • Aug 20, 2009

Some information about <a href="https://www.vitcas.com" target="_blank" rel="nofollow noopener noreferrer">Refractory Materials Manufacturer - Wide Range of Refractories | VITCAS</a> you can find <a href="https://www.vitcas.com" target="_blank" rel="nofollow noopener noreferrer">Refractory Materials Manufacturer - Wide Range of Refractories | VITCAS</a>

Are you sure? This action cannot be undone.
Cancel
eng.

Member • Aug 21, 2009

Thank you very much all

Are you sure? This action cannot be undone.
Cancel